英语翻译研究了碳含量在0.28%、0.35%,0.45%三种中碳低合金钢在空气、盐,水中冷却的过程,并在低温回火处理后得

来源：学生作业帮编辑：作业帮分类：英语作业时间：2024/05/15 11:42:43

英语翻译
研究了碳含量在0.28%、0.35%,0.45%三种中碳低合金钢在空气、盐,水中冷却的过程,并在低温回火处理后得到的组织与机械性能.在中碳低合金钢中含碳量与冷却速度是影响其性能的主要原因,淬火介质是影响其冷却速度的主要原因.当淬火冷却速度低时,例如空淬,中碳低合金钢的含碳量应选0.45%,这样组织中会出现一定量贝氏体.当淬火冷却速度较大时,例如水淬,中碳低合金钢主要以马氏体形式存在,应尽量选择较低碳含量,本文中选择0.28%较优,这样可以避免出现脆性过大的隐针形马氏体.当淬火盐浴等温淬火时,中碳低合金钢出现大量贝氏体,盐浴时间影响不明显.

Research on the carbon content of 0.28%,0.35%,0.45% of carbon in three low-alloy steel in the air,salt,water cooling process,and after tempering at low temperatures has been the organization and mechanical properties.Carbon in the carbon content in low alloy steel and cooling rate affect the performance of the main reasons is the impact of Quenchant the main reason for the cooling rate.When the quenching cooling rate is low,such as air-quenched,low-alloy steel carbon carbon content of 0.45 percent should be elected so that there will be organized a certain amount of bainite.When the quenching cooling rate is high,such as water quenching,low-alloy steel of carbon exist in the form of mainly martensite should be to choose a lower carbon content,0.28 percent in this article better choice,so avoid excessive brittleness of the implicit needle-shaped martensite.When the salt-bath quenching Austempered when in a large number of carbon bainitic low-alloy steel,salt bath time was not obvious.

英语翻译研究了碳含量在0.28%、0.35%,0.45%三种中碳低合金钢在空气、盐,水中冷却的过程,并在低温回火处理后得将钢加热到临界温度以上,保温后从炉中取出在空气中冷却,这个过程是淬火还是正火?还是回火?调质? 在探究氧气在空气中含量的实验中,为什么必须等到红磷冷却后才可以打开弹簧夹?红磷不是迟早都会冷却吗? 刀淬火回火我把刀烧红后在空中停一段时间后放入盐水混合物进行淬火,目测刀完全冷却后拿了出来,现在该怎样回火? 为什么在测定空气中氧气含量的实验中要等装置冷却后才打开弹簧夹在证明氧气在空气中含量的实验中,为什么要等瓶内温度降至室温后【温度冷却后】才能打开弹簧夹用落体法研究机械能守恒定律的实验中，某同学按照正确的操作选得纸带，但在处理纸带的过程中不小心把纸带撕成三个小段，并丢失了在操作氧焊时怎样预防回火:回火怎样处理. 英语翻译水中的各种离子在旱季雨季中的含量会有差异并且各个地点的中的含量也有所不同.本文研究了柴河流域中井水与河道水中八大在测量空气中氧气的含量实验中,为什么待红磷冷却后,打开弹簧夹,烧杯内的水会沿导管进入集气瓶?:-( 高速工具钢淬火后为什么需要进行三次以上回火?在560度回火是否是调质处理在燃烧红磷测定空气中氧气含量的实验中,为什么要等到装置冷却到室温后才打开止水夹