However,based on the ANOVA results shown in TABLE 12 and TABLE 13,which took into account the variability of the SCB test,there was no statistical difference in the means of the fracture toughness data (p-value = 0.729 and 0.154) at a 5 percent significance level.There was also no statistical difference in the means of the fracture energy data measured at -18oC (TABLE 14).However,the difference in the means of the fracture energy data measured at -30oC (TABLE 15) was statistically significant.Further analysis using Tukey’s test showed that only \x0bthe means of the fracture energy data measured at -30oC for two mixtures,including the 40 percent Thiopave mix using the PG 67-22 binder at 2 percent design air voids and the 30 percent \x0bThiopave mix using the PG 58-28 binder at 3.5 percent design air voids,were statistically different.Therefore,it could be said that with the one exception (30 percent Thiopave mix at 3.5 percent design air voids),the effect of using a softer base binder (PG 58-28) in the Thiopave \x0bmixtures was not statistically significant based on the fracture parameters determined in SCB testing.
However,based on the ANOVA results shown in TABLE 12 and TABLE 13,which took into account the variability of the SCB test,there was no statistical difference in the means of the fracture toughness data (p-value = 0.729 and 0.154) at a 5 percent significance level.There was also no statistical difference in the means of the fracture energy data measured at -18oC (TABLE 14).However,the difference in the means of the fracture energy data measured at -30oC (TABLE 15) was statistically significant.Further analysis using Tukey’s test showed that only \x0bthe means of the fracture energy data measured at -30oC for two mixtures,including the 40 percent Thiopave mix using the PG 67-22 binder at 2 percent design air voids and the 30 percent \x0bThiopave mix using the PG 58-28 binder at 3.5 percent design air voids,were statistically different.Therefore,it could be said that with the one exception (30 percent Thiopave mix at 3.5 percent design air voids),the effect of using a softer base binder (PG 58-28) in the Thiopave \x0bmixtures was not statistically significant based on the fracture parameters determined in SCB testing.
然而,基于方差分析结果见表12和表13,它考虑的可变性,渣打银行测试,没有统计上的差异,在手段的断裂韧性数据(假定值= 0.729和0.154)在5%的显著性水平.也没有统计上的差异,在手段的断裂能量数据测量在-18 oc(表14).然而,不同的方式断裂能量数据测量在-30 oc(表15)有统计学意义.菲尔特
英语翻译However,based on the ANOVA results shown in TABLE 12 and
英语翻译we also reported results for aggregated aid based on the
英语翻译The strategy is based on firms in the extreme high and l
英语翻译usually the hole-based system is used as this results in
英语翻译As shown in Table 1 and described below,best value suppl
英语翻译Measurements and model results agreed well on the amplit
英语翻译Security in Automation and Control Systems based on OPC
英语翻译As is shown by the figure/percentage in the table/pictur
英语翻译The results detailed and determination judged in this do
英语翻译The original fashion based on functional needs and moder
英语翻译Based on the brief and visualizations provided,we propos
英语翻译based on the concept of balanced commitment and conserva