以促进剂M和叔丁胺为原料,次氯酸钠为氧化剂,合成硫化橡胶助催剂TBBS的工艺。通过对反应物摩尔配比、氧化剂配比、反应时间和反应温度等反应条件下进行实验,研究各种因素对熔点等的影响规律,进行正交实验探索出最佳合成条件。结果表明,以0. 1 mol促进剂M为准,促进剂M与叔丁胺的摩尔比为1∶1.6 ,促进剂M与次氯酸钠的摩尔比为1∶1.2 ,打浆时间20 min,反应和保温为恒温60摄氏度,在该温度下反应时间为2小时,室温反应10 min 。在此条件下,反应比较平稳、安全,得到产品橡胶促进剂TBBS的熔点高,熔程短,经红外光谱分析,证明合成产物与目的产物结构基本吻合。
以促进剂M和叔丁胺为原料,次氯酸钠为氧化剂,合成硫化橡胶助催剂TBBS的工艺。通过对反应物摩尔配比、氧化剂配比、反应时间和反应温度等反应条件下进行实验,研究各种因素对熔点等的影响规律,进行正交实验探索出最佳合成条件。结果表明,以0. 1 mol促进剂M为准,促进剂M与叔丁胺的摩尔比为1∶1.6 ,促进剂M与次氯酸钠的摩尔比为1∶1.2 ,打浆时间20 min,反应和保温为恒温60摄氏度,在该温度下反应时间为2小时,室温反应10 min 。在此条件下,反应比较平稳、安全,得到产品橡胶促进剂TBBS的熔点高,熔程短,经红外光谱分析,证明合成产物与目的产物结构基本吻合。
这是有道翻译的
In order to promote agent M and tert-butyl d amine as raw materials, sodium hypochlorite as the oxidant, synthetic sulfur rubber help push agent TBBS process. Through of reactant molar ratios, the oxidant ratio, reaction time and reaction temperature under the reaction conditions such as the experimental study of various factors on melting point, such as the influence law of orthogonal experiment exploring the optimal synthetic conditions. The results indicated that the 0. 1 mol acclerant M shall prevail, promoting agents M and uncle mole ratio of butyl amine for 1:1.6, promoting agents M and the molar ratio of sodium hypochlorite 1:1.2, beating time 20 min, response and thermal insulation for constant temperature 60 degrees Celsius in the temperature, reaction time, reaction temperature for 2 hours 10 min. In these conditions, reaction smoothly, safe, and get the goods TBBS melting point of rubber accelerator, melting process short, high by ir analysis, proof synthesis product and objective product structure basic data.
海词翻译的
To promote agents as raw materials M and tert-butylamine, sodium hypochlorite as oxidant, synthetic rubber vulcanization process to help TBBS reminder agent.
Through the mole ratio of oxidant ratio, reaction time and reaction temperature under the experimental conditions to study the various factors on the melting point of law, the orthogonal experiments to explore the best synthesis conditions.
The results showed that 0. 1 mol M prevail accelerator, accelerator M and the molar ratio of tert-butylamine 1:1.6, Accelerator M with sodium hypochlorite mole ratio of 1:1.2, beating time of 20 min, reaction and thermal insulation for the temperature 60 degrees Celsius, the temperature of the reaction time is 2 hours at room temperature for 10 min.
Under these conditions, the reaction is relatively stable, secure, products, rubber accelerator TBBS high melting point, melting range is short, by infrared spectroscopy, synthetic product proved consistent with the purpose of the product structure.
这是我在网上在线翻译的,不知是不是全对,希望帮到你
In order to promote agent M and tert-butyl d amine as raw materials, sodium hypochlorite as the oxidant, synthetic sulfur rubber help push agent TBBS process. Through of reactant molar ratios, the oxidant ratio, reaction time and reaction temperature under the reaction conditions such as the experimental study of various factors on melting point, such as the influence law of orthogonal experiment exploring the optimal synthetic conditions. The results indicated that the 0. 1 mol acclerant M shall prevail, promoting agents M and uncle mole ratio of butyl amine for 1:1.6, promoting agents M and the molar ratio of sodium hypochlorite 1:1.2, beating time 20 min, response and thermal insulation for constant temperature 60 degrees Celsius in the temperature, reaction time, reaction temperature for 2 hours 10 min. In these conditions, reaction smoothly, safe, and get the goods TBBS melting point of rubber accelerator, melting process short, high by ir analysis, proof synthesis product and objective product structure basic data.
海词翻译的
To promote agents as raw materials M and tert-butylamine, sodium hypochlorite as oxidant, synthetic rubber vulcanization process to help TBBS reminder agent.
Through the mole ratio of oxidant ratio, reaction time and reaction temperature under the experimental conditions to study the various factors on the melting point of law, the orthogonal experiments to explore the best synthesis conditions.
The results showed that 0. 1 mol M prevail accelerator, accelerator M and the molar ratio of tert-butylamine 1:1.6, Accelerator M with sodium hypochlorite mole ratio of 1:1.2, beating time of 20 min, reaction and thermal insulation for the temperature 60 degrees Celsius, the temperature of the reaction time is 2 hours at room temperature for 10 min.
Under these conditions, the reaction is relatively stable, secure, products, rubber accelerator TBBS high melting point, melting range is short, by infrared spectroscopy, synthetic product proved consistent with the purpose of the product structure.
这是我在网上在线翻译的,不知是不是全对,希望帮到你
毕业论文摘要要求英文翻译 英语不好的孩子伤不起啊 求英语高手帮忙翻译!
毕业论文的英文摘要,哪个英语高手帮忙翻译一下,不要机器的,谢谢.
毕业论文英文摘要 帮忙翻译下 不要在线翻译的 谢谢 求大神
求英语大神帮我翻译毕业论文的摘要~~
求英语高手翻译!这是毕业论文的摘要,不要网上的直译哦!谢谢!
谁能把这个翻译成英文下面是我写毕业论文的摘要,要翻译成英文,但用在线翻译和有道翻译的不能用,本人英语菜到家 谁能给翻译下
求英语翻译:(这个是毕业论文的摘要,求尽量准确翻译,谢谢)
英语翻译这是毕业论文的摘要翻译,由于本人英文水平有限,现在高分求英文翻译能力好的人士翻译一下下面的文字,注:不要Goog
求翻译,汉译英,英文摘要用的.谢谢大家
毕业论文的中文摘要翻译成英文摘要 本人新手就10个财富值 希望好心人帮忙 急要 谢谢了
求毕业论文英语摘要,不要工具翻译的,哥也会上网.英语牛人
求英文翻译毕业论文摘要